Titanium Plate

Titanium plate is made of 99.95% pure titanium material , which were origined from the best quality raw material in the world - Baoji, Shannxi province. It is also the most important reason for producing the titanium plate.

Specifications:

Size: Cold Rolled (thinkness: 0.3~4.0mm Width: 400~1000mm Length: 1000~3000mm)

Hot Rolled (thinkness: 4.1~60.0mmWidth: 400~3000mm Length: 1000~4000mm)

Standard: ASTM B265, AMS4911, ASTM F67, ASTM F136

Grade: GR1.GR2, GR3, GR5, GR7, GR9, GR12, etc

MOQ: 1 KG

Package: vacuum plastic packing inside and poly-wood case outside

Delivery Time: within 3 to 15 days

Payment: T/T, Paypal, Money Gram, Western Union, L/C

Supply ability: 300tons/month

Port of shipment: Tianjin / Shenzhen

Surface Treatment: polishing surface, acid surface,

Titanium chemical Composition:

Element	Composition,%
	Gr1	Gr2	Gr3	Gr4	Gr5	Gr7	Gr9	Gr11	Gr12
N max	0.03	0.03	0.05	0.05	0.05	0.03	0.03	0.03	0.03
C max	0.08	0.08	0.08	0.08	0.08	0.08	0.08	0.08	0.08
H max	0.05	0.015	0.015	0.015	0.015	0.015	0.015	0.015	0.015
Fe max	0.2	0.3	0.3	0.5	0.4	0.5	0.25	0.2	0.3
O max	0.18	0.25	0.35	0.4	0.2	0.25	0.15	0.18	0.25
Al					5.5-6.75		2.5-3.5
V					3.5-4.5		2.0-3.0
Pd						0.12-0.25

Sample

Free sample --- Small quantity samples are available at any time

Paid sample --- Out of stock or need much money for the sample

Quality Assurance:

---- According to globally recognized standards, such as ASTM, AMS, ASME, JIS, MIL...

---- Provide third-part inspection reports.

-----Visual inspection to check surface quality, ensuring without flaw, black dot and any other defects.

-----Chemical Composition making sure all chemical components can satisfy customer's demands

-----Mechanical Property testing

---- ISO Quality Management System

----SGS test

1. Size

Thermal processing condition (R), Cold-work condition (Y), Annealed (M)

· Thickness: 0.3~60mm

· Width: 400~3600mm

· Length: 100~5600mm

2. Mechanical Properties

Annealed status in room-temperature (20°C)

1. Tensile Strength: σb≥345Mpa(50Ksi)

2. Permanent Elongation stress: σ0.2≥276Mpa(40Ksi)

3. Elongation: δ4D≥20%

4. Reduction of Area: Ψ≥30%

3. Chenical Constituent

Ti	Al	V	Mo	Ni	Pd	Fe	C	N	H	O	Others
Balance	-	-	-	-	-	≤0.30	≤0.08	≤0.03	≤0.01	≤0.25	≤0.40

4. Production Process

The main production process of Titanium Bar are Fmelting -> Forging -> Hot Rolling -> Cold Rolling -> Shearing -> Pickling -> Flattening

NAME	grade 5 Titanium Sheet
GRADE	GR1, GR2, GR5
STANDARD	ASTM B265, GB/T 3621-2007
DIMENSION (MM)	Thk1.0-20* ≥2500*≥6000 MM

1. Metal Chemical Composition:

Grade	N	C	H	Fe	O	Ti
Gr1	0.03	0.08	0.015	0.20	0.18	bal
Gr2	0.03	0.05	0.015	0.30	0.25	bal
Gr5	0.05	0.08	0.015	0.4	0.2	Bal

2. Substrate Metal Mechanical Properties:

Grade	Tensile strength(min)		Yield strength(min)		Elongation (%)
	ksi	MPa	ksi	MPa
Gr1	35	240	25	170	24
Gr2	50	400	40	275	20
Gr5	50	895	40	828	10

3. Applications:

Chemical processing, Medical instruments,

Aerospace, Industry, Navigation, Smelting,

Petrochemical industry, Machining field,

Automobile field, Textile printing and dyeing

Looking for ideal High Purity Titanium Plate Manufacturer & supplier ? We have a wide selection at great prices to help you get creative. All the Titanium Plate in Stock are quality guaranteed. We are China Origin Factory of Pure Titanium Plate Price. If you have any question, please feel free to contact us.

Product Categories : Titanium > Titanium Plate